Features:
Sheet Size 1500mm x 1500mm
Thickness 0.5mm - 3.0mm
Temperature Limit 260°C
Application Industrial Services
Premium quality compressed sheet for gaskets made of mineral fibre, aramide and dispersed inorganic loads mixed in a matrix of high quality type NBR rubber. The material has high compressibility, good tensile strength and low gas permeability. Excellent charactaristics for many industrial services where the high demand of resistance to temperature and pressure are combined.
DVGW (DIN 3535-6 gas supply) DVGW (VP-401 high temperature in gas) WRAS (BS6920 drinking water)
Technical Data | |
---|---|
Density | 1.65 g/cm3 |
Compressibility ASTM F-36 | 7% - 15% |
Recovery ASTM F-36 | >50% |
Transverse Tensile Strength ASTM F-36 A | 12MPa |
Gas Permeability DIN 3535/6 | <1 cm3/min |
Thickness Increase ASTM F-146 | |
ASTM oil Nº3 5h 150ºC | <3% |
ASTM fuel B 5h 20ºC | <7% |
Sheet Size 1500mm x 1500mm
Thickness 0.5mm - 3.0mm
Temperature Limit 260°C
Application Industrial Services
Sheet Size 1500mm x 1500mm
Thickness 0.5mm - 3.0mm
Temperature Limit 260°C
Application Industrial Services
Premium quality compressed sheet for gaskets made of mineral fibre, aramide and dispersed inorganic loads mixed in a matrix of high quality type NBR rubber. The material has high compressibility, good tensile strength and low gas permeability. Excellent charactaristics for many industrial services where the high demand of resistance to temperature and pressure are combined.
DVGW (DIN 3535-6 gas supply) DVGW (VP-401 high temperature in gas) WRAS (BS6920 drinking water)
Technical Data | |
---|---|
Density | 1.65 g/cm3 |
Compressibility ASTM F-36 | 7% - 15% |
Recovery ASTM F-36 | >50% |
Transverse Tensile Strength ASTM F-36 A | 12MPa |
Gas Permeability DIN 3535/6 | <1 cm3/min |
Thickness Increase ASTM F-146 | |
ASTM oil Nº3 5h 150ºC | <3% |
ASTM fuel B 5h 20ºC | <7% |
Sheet Size 1500mm x 1500mm
Thickness 0.5mm - 3.0mm
Temperature Limit 260°C
Application Industrial Services
Premium quality compressed sheet for gaskets made of mineral fibre, aramide and dispersed inorganic loads mixed in a matrix of high quality type NBR rubber. The material has high compressibility, good tensile strength and low gas permeability. Excellent charactaristics for many industrial services where the high demand of resistance to temperature and pressure are combined.
DVGW (DIN 3535-6 gas supply) DVGW (VP-401 high temperature in gas) WRAS (BS6920 drinking water)
Technical Data | |
---|---|
Density | 1.65 g/cm3 |
Compressibility ASTM F-36 | 7% - 15% |
Recovery ASTM F-36 | >50% |
Transverse Tensile Strength ASTM F-36 A | 12MPa |
Gas Permeability DIN 3535/6 | <1 cm3/min |
Thickness Increase ASTM F-146 | |
ASTM oil Nº3 5h 150ºC | <3% |
ASTM fuel B 5h 20ºC | <7% |